Cyanide Free Alkaline Zinc Plating Chemicals Brightener High Throwing Power ZN-265

Cyanide Free Alkaline Zinc Plating Chemicals Brightener High Throwing Power ZN-265

  • High Light

    zinc electroplating chemicals

    ,

    zinc plating brightener

    ,

    Alkaline Zinc Plating Chemicals Brightener

  • Application
    Zinc Plating Process
  • Purity
    99%min
  • Type
    Fastener Zink Plating
  • Other Name
    Zinc Electroplating Brightener,
  • Place of Origin
    China
  • Brand Name
    FENGFAN
  • Model Number
    ZN-265
  • Minimum Order Quantity
    Negotiable
  • Price
    Negotiable
  • Packaging Details
    Standard export packaging
  • Delivery Time
    15-25 work days
  • Payment Terms
    L/C, D/A, D/P, T/T, Western Union, MoneyGram
  • Supply Ability
    200000pcs/day

Cyanide Free Alkaline Zinc Plating Chemicals Brightener High Throwing Power ZN-265

High Throwing Power Cyanide-free Alkaline Zinc Plating

ZN-265

 

ZN-265 alkaline zinc plating additive is a kind of brightener concentrated by a variety of polyamine compound. It can produce a smooth, bright, delicate and flexible zinc plating layer in alkaline non-cyanide zinc plating solution, and can completely replace the traditional cyanide zinc plating.

 

I. Properties

1, Electroplating can be carried out in a wide range of zinc metal content 5.5-18.5 g/L.

2, Can make the workpiece surface bright and decorative even the temperature up to 48 ℃.

3, Excellent covering capacity and dispersing ability in low current region, especially for some complex workpieces for rack plating. Such as pipes, fittings and computer shell.

4, Good dispersion capacity. High current density: low current density can reach 1.5. It can shorten the plating time and reach a minimum standard of coating thickness. Can improve the efficiency of the use of zinc.

5, Good tolerance with the impurities in the bath such as calcium, magnesium, iron, lead, cadmium and chromium.

6, It is suitable for low current density of barrel plating and wide current density range of rack plating.

7, Easy to accept various passivation post treatments.

 

II. Technical Formulation & Operation Condition

Component Physical parameters Consumption
ZnO (g/L) 10~20 (the best 15g/L) /
NaOH (g/L) 100~140 (the best 130g/L) /
Zn-265A brightener (ml/L) 10-14 80~180ml/KAH
Zn-265B additive (ml/L) 0.5-2ml/L 30~80ml/KAH
Zn-265C purifier (ml/L) 2-4ml/L Usually no need add. When high impurities content or adding sodium hydroxide, it should be added properly.

Operation condition: Temperature

Anode area ratio

Anode

Rack plating: Cathode current density

Cathode move

Barrel plating: Cathode current density

Barrel speed

5~52℃

1:1.5~2

0# zinc plate

0.5~8 A/dm2

8~12 time/min

0.5~8 A/dm2

6~8 time/min

/