Environmentally Medium Phosphorus Electroless Nickel Process FF-607

Environmentally Medium Phosphorus Electroless Nickel Process FF-607

1. PRODUCT PERFORMANCE
1. Environment friendly, in line with EU ROHS requirements;
2. The plating solution has good stability and long service life, generally up to 8 MTO;
3. The soldering performance of the layer is excellent, and the copper-plated parts are not leaked;
4. The bonding force is excellent, the bonding force on medium and low carbon steel can reach
350-450MPa, and the bending test can not be peeled;
5. The hardness is high, the hardness as plated can reach 550-600HV, and the hardness can
reach 1000HV after being kept at 400 ℃ for 1 hour;
6. Due to no current, the uniformity of the layer is good, the size is easy to control, and no further
processing is required after plating;
7. The plating speed is 1 micron/3 minutes, the layer is white and bright, and the gloss can be
kept consistent during the service cycle;
8. The layer is micro-magnetic.

2. USAGE
FF-607A: make up and replenishment
FF-607B: make up
FF-607C: replenishment
make new bath
1. Make up amount
FF-607A 50mL/L
FF-607B 120mL/L