FF-5131 Cyanide-free Copper Plating Chemicals for Fast Deposition Stable Process and Uniform Coating

FF-5131 Cyanide-free Copper Plating Chemicals for Fast Deposition Stable Process and Uniform Coating

  • Highlight

    Fast Deposition Copper Plating Chemicals

    ,

    Stable Process Copper Plating Chemicals

    ,

    Uniform Coating Cyanide-free Copper-Zinc Alloy Process

  • Type
    Brightener
  • Use
    Copper Zinc Alloy Plating
  • Characteristic
    Cyanide-free
  • Feature
    Fast Deposition, Stable Process
  • Place of Origin
    CHINA
  • Brand Name
    FENGFAN
  • Model Number
    FF-5131

FF-5131 Cyanide-free Copper Plating Chemicals for Fast Deposition Stable Process and Uniform Coating

FF-5131 Cyanide-Free Copper-Zinc Alloy Process / Copper Plating Chemicals
Product Features
  • This process does not contain sodium (potassium) cyanide, lead, cadmium or other heavy metals
  • Produces uniform, stable coatings with consistent brass appearance
  • Excellent alignment suitable for both roll plating and rack plating
  • Can be used for both surface coloring and thick brass plating (above 10μm)
  • Primarily used in decoration, jewelry, handicrafts, and industrial applications
  • Environmentally friendly alternative to precious metal cyanide plating
  • 30% lower production and operating costs compared to sodium cyanide systems
Process Flow
Copper plating → Recycling → Rinsing → Activation (5~10% Sulphuric acid) → Rinsing → Plating of full bright nickel → Recycling → Rinsing → Activation (5% sulphuric acid) → Rinsing → Pure water rinsing → Electroplating cyanide-free copper-zinc alloy Gold → water washing → passivation → water washing → pure water washing → drying → spraying and baking.
Bath Composition and Operating Conditions
Item Range Optimal
FF-5131M 800~940ml/L 900ml/L
FF-5131A Use for supplement ----
FF-5131B 50~60ml/L 60ml/L
Temperature 35~45℃ 40℃
Time 3~30min 5min
pH 10~11.8 10.8
Dk 0.3~1.0A/dm²
Anod Brass plate (copper : zinc ratio 70:30)
Stirring method Cathodic movement / plating flow
Cycle filtering Continuous filtration, the capacity of cotton core is 2~3 times per hour