Send Message
Wuhan Fengfan International Trade Co.,Ltd. 86-27-85615818 info@fengfan.net
Palladium Cobalt Alloy Process Approximately 80-90% Palladium 10-20% Cobalt FF-Pd108

Palladium Cobalt Alloy Process Approximately 80-90% Palladium 10-20% Cobalt FF-Pd108

  • Highlight

    Palladium Cobalt Alloy Process

    ,

    90% Palladium Cobalt Alloy Process

    ,

    20% Cobalt Alloy Plating Chemicals

  • Type
    Brightener
  • Use
    Palladium Cobalt Alloy
  • Item
    Chemical Auxiliary Agent
  • Feature
    Bright, Ductile And White Coatings
  • Place of Origin
    CHINA
  • Brand Name
    FENGFAN
  • Model Number
    FF-Pd108

Palladium Cobalt Alloy Process Approximately 80-90% Palladium 10-20% Cobalt FF-Pd108

Palladium Cobalt Alloy Process ; Approximately 80-90% Palladium, 10-20% Cobalt ; FF-Pd108

 

1. Specific Properties and Application

FF-PD108 palladium-cobalt alloy process can produce bright, ductile and white coatings (approximately 80-90% palladium, 10-20% cobalt) in a slightly alkaline bath, which is suitable for rack plating and barrel plating operations. The coating is snow-white, rich in gloss, and has a low-porosity coating to improve the protective coating and prevent the corrosion of the substrate metal coating.

Coating characteristics: the coating is snow-white and shiny, corrosion-resistant

Metal content: 80-90% palladium, 10-20% cobalt

Density: 10-11g/cm³

 

2. Technical Formulation

  Range Standard
Palladium metal 0.5-1.5g/L 1g/L
Cobalt metal 0.1-0.3g/L 0.2g/L
Temperature 33-38℃ 35℃
PH(35℃) 8.0-8.6 8.3
Mixing mode Mechanical stirring and bath circulation
Current density 0.5-1.5A/dm2 1.0A/dm2
Palladium metal deposition rate At 1A/dm2, 1um can be plated in 4.5 minutes, and 0.025g palladium-cobalt alloy can be plated per ampere minute.